From: Durability of fluoropolymer and antibacterial finishes on woven surgical gown fabrics
Experimental conditions | Impact penetration (g) | Hydrostatic pressure (cm) | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Antibacterial finish (%) | Water repellent finish (%) | A | B | C | D | E | F | A | B | C | D | E | F | |
1. | 0 | 1 | 0.91 | 1.32 | 3.51 | 0.56 | 0.42 | 0.86 | 14.5 | 14.0 | 7.9 | 17.0 | 18.5 | 15.5 |
2. | 0 | 4 | 0.70 | 0.68 | 2.54 | 0.45 | 0.31 | 0.54 | 22.5 | 20.6 | 13.6 | 25.3 | 28.5 | 20.5 |
3. | 0 | 7 | 0.49 | 0.64* | 1.30 | 0.35 | 0.24 | 0.43 | 25.7 | 22.9 | 16.1 | 27.0 | 32.7 | 22.3 |
4. | 1 | 1 | 0.96 | 1.29 | 3.27 | 0.53 | 0.41 | 0.81 | 15.2 | 13.9 | 9.3 | 18.2 | 19.0 | 16.5 |
5. | 1 | 4 | 0.72 | 0.61 | 2.52 | 0.41 | 0.27 | 0.55 | 23.2 | 21.4 | 14.7 | 25.8 | 29.5 | 21.0 |
6. | 1 | 7 | 0.46 | 0.53 | 1.30 | 0.29 | 0.24 | 0.38 | 26.6 | 23.5 | 16.8 | 27.8 | 32.3 | 22.9 |
7. | 1.5 | 1 | 0.96 | 1.06 | 3.12 | 0.47 | 0.37 | 0.84 | 15.5 | 15.3 | 9.5 | 17.9 | 19.0 | 16.5 |
8. | 1.5 | 4 | 0.64 | 0.59 | 2.30 | 0.39 | 0.28 | 0.51 | 24.4 | 22.3 | 15.1 | 25.9 | 29.5 | 21.4 |
9. | 1.5 | 7 | 0.41 | 0.56 | 1.19 | 0.28 | 0.25 | 0.36 | 28.0 | 23.9 | 17.1 | 27.8 | 34.7 | 23.1 |
10. | 3 | 1 | 0.89 | 0.90 | 3.16 | 0.43 | 0.36 | 0.76 | 16.1 | 15.9 | 10.3 | 18.7 | 19.5 | 17.3 |
11. | 3 | 4 | 0.57 | 0.54 | 2.01 | 0.36 | 0.24 | 0.39 | 26.6 | 23.0 | 15.7 | 26.0 | 29.0 | 22.0 |
12. | 3 | 7 | 0.42 | 0.53* | 1.03 | 0.23 | 0.21 | 0.30 | 29.7 | 24.2 | 17.5 | 29.0 | 36.0 | 24.0 |
13. | 1 | 0 | 1.56# | 1.69# | 4.57 | 0.89 | 0.59* | 1.03 | 6.8# | 6.1 | 5.5*# | 5.8# | 9.2# | 4.9 |
14. | 1.5 | 0 | 1.49# | 1.62* | 4.49 | 0.82* | 0.58* | 0.96 | 6.9*# | 7.1 | 5.4*# | 6.7*# | 9.0*# | 4.8* |
15. | 3 | 0 | 1.43* | 1.54 | 4.23 | 0.79* | 0.54* | 0.91 | 7.7* | 7.2* | 6.3* | 8.0* | 11.1 | 5.7 |
16. | 0 | 0 | 1.53 | 1.72 | 4.97 | 0.97 | 0.73 | 1.17 | 6.5 | 5.3 | 4.5 | 6.0 | 9.0 | 4.3 |