Sample code | Tensile strength (N) | Work of rupture (NÂ m) | Impact resistance (KJ) | ||
---|---|---|---|---|---|
Course direction | Wale direction | Course direction | Wale direction | ||
PSL | 54 | 89 | 2.23 | 2.27 | 4.6 |
55 | 91 | 2.41 | 2.7 | 4.8 | |
51 | 90 | 2.13 | 2.49 | 4.7 | |
56 | 95 | 2.52 | 2.9 | 5.2 | |
54 | 92 | 2.38 | 2.79 | 4.8 | |
Average | 54 | 91.4 | 2.334 | 2.63 | 4.82 |
SD | 1.871 | 2.302 | 0.154 | 0.251 | 0.228 |
cv% | 3.464 | 2.519 | 6.600 | 9.555 | 4.731 |
PSH | 66 | 120 | 2.9 | 3.65 | 7 |
72 | 127 | 3.16 | 3.82 | 7.3 | |
68 | 123 | 3 | 3.78 | 7.1 | |
69 | 121 | 3.09 | 3.7 | 7.1 | |
67 | 122 | 2.99 | 3.76 | 7.1 | |
Average | 68.4 | 122.6 | 3.028 | 3.742 | 7.12 |
SD | 2.302 | 2.702 | 0.100 | 0.067 | 0.110 |
cv% | 3.366 | 2.204 | 3.298 | 1.797 | 1.539 |
RDL | 59 | 261 | 2.73 | 7.24 | 14.2 |
57 | 258 | 2.56 | 7.1 | 14.1 | |
58 | 260 | 2.67 | 7.18 | 14.1 | |
60 | 272 | 2.8 | 7.37 | 14.8 | |
56 | 249 | 2.41 | 6.93 | 13.5 | |
Average | 58 | 260 | 2.634 | 7.164 | 14.14 |
SD | 1.581 | 8.216 | 0.153 | 0.164 | 0.462 |
cv% | 2.726 | 3.160 | 5.811 | 2.286 | 3.264 |
RDH | 60 | 269 | 2.8 | 7.33 | 15.2 |
62 | 274 | 2.86 | 7.42 | 15.6 | |
59 | 268 | 2.73 | 7.29 | 14.7 | |
63 | 281 | 2.9 | 7.73 | 15.8 | |
61 | 271 | 2.81 | 7.36 | 15.3 | |
Average | 61 | 272.6 | 2.82 | 7.426 | 15.32 |
SD | 1.581 | 5.225 | 0.064 | 0.176 | 0.421 |
cv% | 2.592 | 1.917 | 2.284 | 2.376 | 2.746 |
CSL | 109 | 102 | 3.9 | 2.94 | 5.9 |
111 | 106 | 3.96 | 2.99 | 6.1 | |
115 | 108 | 4 | 3.05 | 6.2 | |
120 | 110 | 4.2 | 3.12 | 6.5 | |
116 | 109 | 4.07 | 3.09 | 6.4 | |
Average | 114.2 | 107 | 4.026 | 3.038 | 6.22 |
SD | 4.324 | 3.162 | 0.115 | 0.073 | 0.239 |
cv% | 3.787 | 2.955 | 2.862 | 2.412 | 3.838 |
CSH | 113 | 123 | 3.99 | 4.24 | 7.5 |
120 | 132 | 4.23 | 4.31 | 8.4 | |
112 | 119 | 3.98 | 4.16 | 7.3 | |
118 | 127 | 4.1 | 4.46 | 8 | |
115 | 125 | 4.01 | 4.3 | 7.9 | |
Average | 115.6 | 125.2 | 4.062 | 4.294 | 7.82 |
SD | 3.362 | 4.817 | 0.105 | 0.110 | 0.432 |
cv% | 2.908 | 3.847 | 2.590 | 2.570 | 5.530 |
CDL | 109 | 187 | 4.78 | 5.42 | 9.5 |
106 | 183 | 4.73 | 5.39 | 9 | |
110 | 192 | 4.8 | 5.52 | 10.1 | |
112 | 195 | 4.86 | 5.6 | 10.8 | |
108 | 191 | 4.79 | 5.49 | 9.8 | |
Average | 109 | 189.6 | 4.792 | 5.484 | 9.84 |
SD | 2.236 | 4.669 | 0.047 | 0.083 | 0.673 |
cv% | 2.051 | 2.463 | 0.972 | 1.518 | 6.840 |
CDH | 127 | 206 | 6.19 | 6.24 | 13.6 |
124 | 201 | 6.08 | 6 | 13.3 | |
128 | 215 | 6.22 | 6.39 | 13.8 | |
132 | 220 | 6.32 | 6.61 | 14.1 | |
126 | 212 | 6.11 | 6.35 | 13.5 | |
Average | 127.4 | 210.8 | 6.184 | 6.318 | 13.66 |
SD | 2.966 | 7.463 | 0.095 | 0.223 | 0.305 |
cv% | 2.328 | 3.540 | 1.537 | 3.528 | 2.232 |