International Journal of Interdisciplinary Research
From: Assessment of durable press performance of cotton finished with modified DMDHEU and citric acid
No. | Modified DMDHEU (gpl) | MgCl2 (% ow resin) | SS (gpl) | PE (gpl) | Curing temperature (°C) | Curing time (min) | TCRA | Tensile strength (% retention) | Tear strength (% retention) | Bending length (cm) | WI | AP (cm3/cm2/s) | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Warp | Weft | Warp | Weft | Warp | Weft | ||||||||||
UN | Â | Â | Â | Â | Â | Â | 155 | 100 | 100 | 100 | 100 | 2.3 | 1.52 | 78.80 | 17.96 |
1 | 50 | 25 | 12.5 | 20 | 160 | 4 | 228 | 73.74 | 67.2 | 85.29 | 81.99 | 1.95 | 1.58 | 79.42 | 14.77 |
2 | 60 | 20 | 10 | 20 | 160 | 3 | 222 | 71.33 | 69.2 | 86.19 | 84 | 2.1 | 1.6 | 80.49 | 14.32 |
3 | 60 | 20 | 10 | 20 | 160 | 5 | 240 | 73.03 | 63.71 | 86.71 | 84.15 | 2.04 | 1.58 | 79.95 | 15.42 |
4 | 60 | 20 | 10 | 15 | 160 | 4 | 253 | 74.36 | 69.46 | 80.16 | 82.32 | 2 | 1.49 | 79.2 | 14.82 |
5 | 60 | 20 | 12.5 | 15 | 160 | 5 | 257 | 70.96 | 61.27 | 83.92 | 80.74 | 2.13 | 1.56 | 79.87 | 14.92 |
6 | 60 | 20 | 12.5 | 20 | 160 | 4 | 245 | 74.18 | 66.88 | 87.5 | 82.36 | 2.07 | 1.6 | 79.48 | 14.46 |
7 | 60 | 20 | 15 | 20 | 160 | 3 | 239 | 73.79 | 69.4 | 86.99 | 83.1 | 2 | 1.56 | 78.97 | 14.82 |
8 | 60 | 20 | 15 | 20 | 160 | 5 | 251 | 75.19 | 70.16 | 85.49 | 83.8 | 2.05 | 1.53 | 79.97 | 15.51 |
9 | 60 | 20 | 12.5 | 25 | 160 | 3 | 242 | 71.95 | 63.27 | 89 | 84.14 | 2.05 | 1.54 | 81.46 | 15.45 |
10 | 60 | 20 | 12.5 | 25 | 160 | 5 | 248 | 72.46 | 66.94 | 88.12 | 84.87 | 2.0 | 1.59 | 80.36 | 15.63 |
11 | 60 | 20 | 15 | 25 | 160 | 4 | 263 | 77.03 | 62.78 | 87.89 | 83.69 | 1.9 | 1.48 | 80.19 | 15.21 |
12 | 60 | 25 | 12.5 | 20 | 170 | 4 | 239 | 68.13 | 59.88 | 78.79 | 80.02 | 2.1 | 1.55 | 79.9 | 15.77 |
13 | 70 | 15 | 12.5 | 20 | 160 | 4 | 243 | 70.61 | 63.16 | 88.03 | 78.07 | 2.1 | 1.53 | 79.78 | 14.02 |
14 | 70 | 25 | 12.5 | 20 | 160 | 4 | 256 | 67.29 | 60.18 | 81.31 | 79.98 | 2.1 | 1.53 | 80.57 | 14.99 |
15 | 70 | 20 | 12.5 | 20 | 170 | 4 | 248 | 65.2 | 57.37 | 77.63 | 76.09 | 2.13 | 1.6 | 80.05 | 14.43 |