From: Performance of wearables and the effect of user behavior in additive manufacturing process
AM process /material | Layer thickness (mm) | Part orientation | Postprocess stage | Material quality | Flexural strength (MPa) | Impact strength (KJ/m2) | Compressive strength (MPa) | Yield strength (MPa) | Elongation (%) | Ref. |
---|---|---|---|---|---|---|---|---|---|---|
LS/polycaprolactone | Â | Parallel | Â | Â | Â | Â | 38.7 | 12.5 | Â | Eshraghi and Das (2010) |
Perpendicular | 38.8 | 10.3 | ||||||||
LS/Nylon12 | 02-Jun | YX | Â | Â | Â | Â | Â | Â | 17.5 | Majewski and Hopkinson (2011) |
YZ | 17 | |||||||||
ZY | 11 | |||||||||
LS/Nylon12 | Â | Â | Â | L_Virgin | Â | Â | Â | Â | 4 | Zarringhalam et al. (2006) |
L_Refresher | 7.5 | |||||||||
L_Used | 12.5 | |||||||||
T_Virgin | 14 | |||||||||
T_Refresher | 19 | |||||||||
LS/HIPS | Â | Â | Infiltrating | Â | 18.93 (20.48 after infiltrating) | 3.3 (6.5 after infiltrating) | Â | Â | 5.79 (5.98 after infiltrating) | Yan et al. (2010) |
HIPS.epoxy | 30.69 | 3.9 | 6.44 | |||||||
PA12 | 50.3 | 30.4 | 20.83 | |||||||
PA12.ORECa | 67.3 | 33.8 | 18.2 | |||||||
Nanosilica/PA12 | – | 40.2 | 20.07 |