International Journal of Interdisciplinary Research
Table 5 Influential SL and material jetting process parameters on tensile properties and hardness
From: Performance of wearables and the effect of user behavior in additive manufacturing process
AM process /material | Layer thickness (mm) | Part orientation | Other parameters | Postprocess stage | Tensile strength (MPa) | Young’s modulus, E (MPa) | Hardness | Ref. | ||
|---|---|---|---|---|---|---|---|---|---|---|
PJ/ROMa | Â | Flat-X | Â | Â | 58.58 | Â | Â | Das et al. (2018) | ||
Flat-45 | 57.62 | |||||||||
Flat-Y | 53.82 | |||||||||
Vert-X | 54.26 | |||||||||
Vert-45 | 56.32 | |||||||||
Vert-Y | 53.4 | |||||||||
SL/TSRb, Somosc, Accurad | 0.15/0.1/0.1 | Horizontal, vertical |  |  | 42–56 | 49–71 |  | 97 | Kim and Oh (2008) | |
FDM/ABSe | 0.254 | 17–50 | Nov-25 |  | ||||||
LS/PAf | 0.1/0.15 | 29–49 | 26–39 |  | ||||||
PJ/Epoxy resin | 0.016 | 62 for horizontal | 29 for vertical | Â | ||||||
PJ/ABPg | Â | ZX | Â | Â | 58.28 | Â | Â | 80.23 | Kesy and Kotlinski (2010) | |
XZ | 60.44 | 77.78 | ||||||||
XY | 41.65 | 77.18 for Shore | ||||||||
PJ/ROMa, ABPg |  |  |  | Room T, liquid nitrogen T, immersed in liquid helium | 32–36 |  | 2497–8876 |  | Weiss et al. (2015) | |
FDM/ABS | 32–43 | 2583–5570 | ||||||||
PJ/ROMa | 3.22–3.66 | XYZ | Part spacing: tight vs. far |  | 35.3 | 29 | 1665 | 1719 |  | Barclift and Williams (2012) |
YXZ | 32.3 | 26 | 1501 | 1577 | ||||||
YZX | 31.2 | 24.2 | 1696 | 1176 | ||||||
XZY | 37.8 for tight | 22.9 for far | 1874 for tight | 1284 for far | ||||||