Table 9 Influential FDM process parameters on compressive and yield strengths and elongation at break

AM process /material	Layer thickness (mm)	Number of shell	Part orientation	Raster angle (°)	Compressive strength (MPa)	Yield strength (MPa)		Elongation (%)	Ref.
FDM/PLA^a	0.1		XYZ	90/180		Apr-20			Torres et al. (2016)
	0.3		XZY	45/135		2.3–14
			YZX			4.8–32.5
						2.3–32 for 90/180
						2.24–25.5 for 45/135
FDM/ABS^b				45/− 45		10.4			Es-Said et al. (2000)
				0		16.3
				45		6.6
				90		7.9
				45/0		13.6
FDM			Horizontal, vertical, diagonal	45/− 45	41.3				Lee et al. (2007)
FDM			Horizontal, vertical, diagonal	45/− 45	37				Lee et al. (2007)
FDM/PLA^a				0				6.52	Zhang et al. (2019)
				90				5.58
				45				6.31
				0/90				5.89
				− 1				6.04
FDM/PC^c	4.97–5	0.197		0		18.62		1.57	Hill and Haghi (2014)
				15		16.89		1.64
				30		19.51		2.14
				45		17.79		2.64
				60		27.3		3.17
				75		34.47		2.81
				90		40.2		3.89
FDM/ABS^b			Longitudinal, transverse	0, 90, 45, − 45		24.4–17.9			Rodriguez et al. (2000)
FDM/ABS^b			Longitudinal, transverse	0, 90, 45, − 45		13.6–13.4			Rodriguez et al. (2000)
FDM/ABS^b				Honeycomb, line pattern		14.5	20–32.5		Ebel and Sinnemann (2014)
PLA^a				Honeycomb, line pattern		18–22 for honeycomb	42 for line pattern		Ebel and Sinnemann (2014)